Class 130 Polyurethane with Self-Bonding Overcoat Round Copper Magnet Wire for Solderable Applications. The self-bonding overcoat is often thermoplastic or activated by heat or solvents to adhere to itself when wound tightly, eliminating the need for external binding materials.
Specifications
| Insulation materials | The conductor shall be coated with a dual film. The underlying coating is based on polyurethane resins. The superimposed coating is based on resins that are self-bonding in character. |
| Dimensions | Type 1: 25-52 AWG in accordance with 0.0292mm-0.516mm Type 2: 25-50 AWG in accordance with 0.0406mm-0.538mm |
| Certificate | MW 130-C |
| Thermal Class | 130 |
Properties
| Adherence and flexibility | No cracks visible in the film coating |
| Elongation | Not less than the value in 5-38 |
| Heat shock | No cracks visible in the film coating after conditioning at 175ºC |
| Springback | Not greater than the value in Type 1 42-66；Type 2 46-70 |
| Dielectric breakdown | 25-37 AWG: not less than the value in Type 1 1360v-2640v；Type 2 2270v-4740v 38-51 AWG: not less than the value in Type 1 130v-500v；Type 2 275v-950v |
| Continuity | 25-44 AWG: max number of discontinuities in accordance with Type 1 350-1000；Type 2 500-1500 45-52 AWG: max number of discontinuities in accordance with Type 1 25；Type 2 10 |
Solderability
Covered with continuous film of solder after immersion within the time and temperature specified:
| AWG Size | Temperature | Type 1 | Type 2 |
| 25-29.5 | 390°C | 5 seconds | 6 seconds |
| 30-36 | 390°C | 4 seconds | 5 seconds |
| 37-46 | 390°C | 3 seconds | 4 seconds |
| 47-52 | 360°C | 2 seconds | 3 seconds |
Periodic conformance tests
| Thermoplastic Flow | Median not less than 170ºC |
| Dielectric breakdown at rated temperature | Average not less than 75% of the value required at room temperature |
| Bond strength at room temperature | 36 AWG: no separation of turns other than the first or last turn |
| Bond strength at elevated temperature | Bond conditions and strength requirements as agreed between customer and supplier |
Bond strength at room temperature
26 AWG: no break in the coil specimen when subjected to the load specified in：
| AWG | Mandrel Diameter* | Maximum | Test Load* | |||||||
| WindingTension | Bonding Load* | After HeatBonding | After SolventBonding | |||||||
| inches | mm | grams | newtons | grams | newtons | kilograms | newtons | kilograms | newtons | |
| 26 | 0.157 | 3.99 | 200 | 2.0 | 76.0 | 0.75 | 1.6 | 15.7 | 0.80 | 7.85 |